shrinkages

英

美

(shrinkage 的复数) n. 收缩, 收缩量, 减低
[化] 起皱; 收缩; 收缩量
shrinkage的复数

化学

双语例句

• On the basis of temperature field numeric emulating and combining with dynamic dividing technology of melting pool isolated region, this article used G/ r~ ( 1/ 2) method to predict possible shrinkages and dispersed shrinkages that may appear in solidification process.
  在一般铸件温度场数值模拟的基础上，采用G/R~（1/2）法并结合熔池孤立域的动态划分技术对凝固过程中可能出现的缩松缩孔进行了数值模拟；
• If semi-rigid base course material shrinkages trains by the function of temperature contraction or aridity resistance exceed the ultimate tensile strain that the material what itself can bear, it will fracture, and influence the serviceability of the pavement.
  但半刚性基层材料在温度作用或失水作用下产生的收缩应变一旦超过材料自身所能承受的极限拉应变，就会发生开裂，影响路面的使用性能。
• The influences of initial temperatures and the sizes of clusters on the coalescence were revealed by calculating the shrinkages and aspect ratios and by tracking the snapshots of the system configures.
  通过对并合体系的收缩因子、纵横比率计算，以及体系构型的跟踪记录，揭示了团簇的初始温度和团簇的尺寸对并合过程影响的一般规律。
• At a fixed carbonization temperature, the shrinkages of tangential and radial directions were higher than that of axial direction.
  在相同炭化温度下，竹材炭化过程中切向和径向的收缩率高于轴向。
• In physical and mechanical indexes, the basic density, air-dried density, compression strength parallel to grain, MOR, MOE and toughness of mature wood are higher than that of juvenile wood. The shrinkages of juvenile wood are higher than that of mature wood.
  在物理力学性质指标中成熟材的基本密度、气干密度、顺纹抗压强度、抗弯强度、抗弯弹性模量及冲击韧性高于幼龄材；而幼龄材全缩率高于成熟材。
• The research of early age shrinkages of concrete is very important for the solutions of early age cracking of concrete engineering, especially for high performance concrete.
  研究早龄期收缩对于解决混凝土工程，尤其是高性能混凝土的早期开裂具有重要意义。
• The strength of popular cement at 3d and 28d be equivalent to high C3S cement only when it had high specific surface area, but its drying shrinkages was more than that of high C3S cement at the same curing and drying condition.
  普通水泥只有在很高的比表面积时，3d和28d强度才和高C3S水泥相当，但其干缩比高C3S水泥大得多。
• The effects of carbonization temperature and time on shrinkages of PAN-CHF and PAN-ACHF, activation yield, specific surface area and adsorption capacity were investigated.
  考察了炭化温度和炭化时间对PAN-CHF的收缩率、PAN-ACHF的收缩率、活化收率、比表面积和吸附性能的影响。
• The shrinkages of the different composition zinc matrix alloys were measured by the self made linear shrinkage measurer.
  对模具用不同配比的锌基合金进行了收缩率的测定。
• In order to ensure the forming accuracy of castings, it is necessary to consider the compensation for the shrinkages in the mould cavity for turbine blades brought by the solidification process.
  为了保证精铸件的成形精度，制造所用的模具型腔必须对铸件的收缩变形进行补偿。